What is ASTM A217?
ASTM A217. STANDARD SPECIFICATION FOR STEEL CASTINGS, MARTENSITIC STAINLESS AND ALLOY, FOR PRESSURE-CONTAINING PARTS, SUITABLE FOR HIGH-TEMPERATURE SERVICE.
What is ASTM A217 CA15?
ASTM A217 Grade CA15 Heat-Treated – Martensitic Stainless Steel – Matmatch.
What is A217 WC9 material?
WC9 Valves are made under ASTM A217 specification which covers low alloy valves that can operate under high temperatures and pressures. The alloy group can be made up of carbon, manganese, phosphorus, sulfur, silicon, chromium and molybdenum in the composition.
What is ASTM A182 F22?
Grade 22 of the ASTM A182 alloy steel is a low-alloy steel that contains 2.25% chromium. Often used as base metal for clad components, the F22 is also used in the oil patch wellhead applications for products such as hangers, connectors, and block valves, among others.
What is C5 material?
C5 Valves are made up of a 5% chromium 1/2 % molybdenum alloy. The material is suitable for high temperature refinery services. The most applications of this type of valves can be seen in the oil and gas, petroleum and offshore and onshore oil drilling applications.
What is C12 material?
C12 Valves are used for high temperature erosive refinery services. The material is made up of 9% chromium and 1% molybdenum. The material is made up of carbon, manganese, phosphorus, sulfur, silicon with chromium and molybdenum.
What is CA6NM material?
What is CA6NM Stainless Steel? CA6NM belongs to martensitic stainless steel, also called hydroelectric steel. Molybdenum is added under quenching and tempering conditions to prevent rust. Due to its good toughness, it can be used at temperatures ranging from -60 ℃ to +300 ℃.
What is WC9?
Grade WC9 is covered by ASTM A217 standard; it’s a good Chromium Molybdenum steel for Sand Casting and Investment Casting purpose. ASTM A217 / A217M – 14 Standard Specification for Steel Castings, Martensitic Stainless and Alloy, for Pressure-Containing Parts, Suitable for High-Temperature Service.
What is A217 C5?
ASTM A217 Gr. C5 Valves are made up of a 5% chromium 1/2 % molybdenum alloy. The material is suitable for high temperature refinery services. The most applications of this type of valves can be seen in the oil and gas, petroleum and offshore and onshore oil drilling applications.